2024 Aluminum Bar Stock - Aircraft Aluminum

aluminum alloy 2024

2024 Aluminum Rod Properties

  • Grade: Aerospace-grade aluminum
  • Series: Al-Cu-Mg series aluminum alloy
  • Density: 2.80g/cm3.
  • Modulus of elasticity: Stretch 72. 4GPa (10. 5×106psi), Compression 73.8GPa (10.7×106psi)
  • Annealing Temperature: 413 °C
  • Liquidus: 638 °C (1180 °F)
  • Thickness and size: 2024 Aluminum Aound Bar can be customized according to needs
Product Details

2024 Aluminum Rod

The 2024 aluminum alloy is primarily composed of aluminum, copper, and small amounts of other elements such as manganese, magnesium, and trace elements. Copper is the main alloying element, contributing to the alloy’s high strength and hardness.

2024 aluminum rods have impressive mechanical properties. The typical tensile strength of 2024 aluminum ranges from 300 to 500 MPa (43,500 to 72,500 psi), while the yield strength ranges from 195 to 470 MPa (28,000 to 68,000 psi). These values can vary depending on the specific heat treatment applied.

 

2024 Aluminum Bar Application

The aerospace industry extensively utilizes 2024 aluminum bars due to their excellent strength and lightweight properties. They are commonly used in the construction of aircraft structural components, including wing spars, bulkheads, and fuselage frames. The high strength and machinability of 2024 aluminum make it a reliable choice for demanding aerospace applications.

2024 aluminum rod material properties

Chemical composition

Si

Fe

Cu

Mn

Mg

Cr

Zn

Ti

Zr

Other

Al

Content(%)

0.5

0.5

3.8-4.9

0.30-0.90

0.30-0.90

0.10

0.25

0.15

0.2

Remainder

Request a Quote​​

If you require any assistance, we kindly request you to complete the form provided below. Our dedicated sales team will promptly reach out to you, and rest assured, you can expect a response to your inquiry within a maximum of 12 hours.

+86 0411-8683 8503

Aluminum Land available from 00:00 – 23:59

Address :Room A306, Building#12, Qijiang Road, Ganjingzi

Email : info@goseamarine.com

Ask for Help?

Let's have a chat

Ask for Quotation

Fill out the form below